| 1. | Study of the bioglass - ceramic prepared by sol - gel processing
凝胶法制备生物微晶玻璃的研究进展
|
| 2. | Preparation of bioglass ultrafine powder by sol - gel - self - propagating process
溶胶凝胶自蔓延法制备生物玻璃超细粉
|
| 3. | Porous bioglass material was prepared by attempting to add pore former
摘要尝试采用添加造孔剂的方法制备了多孔生物玻璃材料。
|
| 4. | Biomimetic scaffold composite bioglass - collagen - phosphatidyl serine - hyaluronic acid in the repair of rabbit radius defect
透明质酸复合支架修复兔桡骨缺损
|
| 5. | Bioactive substance such as hydroxyapatite ( ha ) and bioglass are coated on their surfaces in order to improve the bond between the implants and bone tissue
为改善其植入后与骨组织的结合，常在其表面涂覆一层具有生物活性的物质，如羟基磷灰石和生物玻璃等。
|
| 6. | The material was sintered at 1050 for three hours to get the porous artificial bone , that its apparent porosity was54 % , its volume density was 1 . 28 g / cm3 , and its bending strength was 13 . 25mpa . the results showed that the sintering temperature was reduced by adding bioglass
本研究采用含生物玻璃前驱体粉末原料，添加柠檬酸造孔剂，模压成型，在1050烧结保温3小时，获得了显气孔率为54 、体积密度为1 . 28s cm ~ 3 、抗弯强度为13 . 25mpa的多孔hap人工骨材料。
|